Aluminum Dihydride Complexes and their Unexpected Application in Atomic Layer Deposition of Titanium Carbonitride Films

03 May 2018, Version 1
This content is a preprint and has not undergone peer review at the time of posting.

Abstract

Aluminum dihydride complexes containing amido-amine ligands were synthesized and evaluated as potential reducing precursors for thermal atomic layer deposition (ALD). Highly volatile monomeric complexes AlH2(tBuNCH2CH2NMe2) and AlH2(tBuNCH2CH2NC4H8) are more thermally stable than common Al hydride thin film precursors such as AlH3(NMe3). ALD film growth experiments using TiCl4 and AlH2(tBuNCH2CH2NMe2) produced titanium carbonitride films with a high growth rate of 1.6-2.0 Å/cycle and resistivities around 600 μΩ·cm within a very wide ALD window of 220-400 °C. Importantly, film growth proceeded via self-limited surface reactions, which is the hallmark of an ALD process. Root mean square surface roughness was only 1.3 % of the film thickness at 300 °C by atomic force microscopy. The films were polycrystalline with low intensity, broad reflections corresponding to the cubic TiN/TiC phase according to grazing incidence X-ray diffraction. Film composition by X-ray photoelectron spectroscopy was approximately TiC0.8N0.5 at 300 °C with small amounts of Al (6 at%), Cl (4 at%) and O (4 at%) impurities. Remarkably, self-limited growth and low Al content was observed in films deposited well above the solid-state thermal decomposition point of AlH2(tBuNCH2CH2NMe2), which is ca. 185 °C. Similar growth rates, resistivities, and film compositions were observed in ALD film growth trials using AlH2(tBuNCH2CH2NC4H8).

Keywords

atomic layer deposition
thin films
aluminum hydrides
aluminum

Supplementary materials

Title
Description
Actions
Title
SI AlH2 Complexes KJB
Description
Actions

Comments

Comments are not moderated before they are posted, but they can be removed by the site moderators if they are found to be in contravention of our Commenting Policy [opens in a new tab] - please read this policy before you post. Comments should be used for scholarly discussion of the content in question. You can find more information about how to use the commenting feature here [opens in a new tab] .
This site is protected by reCAPTCHA and the Google Privacy Policy [opens in a new tab] and Terms of Service [opens in a new tab] apply.