![Author ORCID: We display the ORCID iD icon alongside authors names on our website to acknowledge that the ORCiD has been authenticated when entered by the user. To view the users ORCiD record click the icon. [opens in a new tab]](https://chemrxiv.org/engage/assets/public/chemrxiv/images/logos/orcid.png)
Abstract
Silicon carbide reinforced multicomponent high entropy diboride-based particulate composites (HEB-SiC) were fabricated by spark plasma sintering at 1800°C using diboride powders prepared from boro-carbothermal reduction method to investigate the influence of the addition of SiC (SiC content = 20, 40 vol%) on the microstructural evolution, oxidation, and exposure to arc-jet behaviour was reported. SiC has been found to improve the densification of pristine diboride, with attainment of a maximum of ~ 98% relative density for SiC content of 40 vol%. A percolating network of SiC grains in the HEB matrix was observed in the case of composites with 40% volume fraction of SiC. The oxidative behavior at 1400°C in air revealed excellent improvement of oxidation resistance of 20 vol% SiC reinforced composite as compared to other sintered specimens. Arc-jet testing on 20 vol% SiC reinforced composite revealed no structural deformity with very minute-scaled formation of surface oxide layers. These results indicate that the addition of 20 vol% SiC in a diboride matrix can contribute to the optimal preparation of high entropy diboride-based ceramics with balanced mechanical properties with improved oxidation resistance.