Mechanics of lithium metal at the nanoscale

01 September 2022, Version 1
This content is a preprint and has not undergone peer review at the time of posting.

Abstract

The fracture of ceramic solid electrolytes, driven by the plating of lithium within cracks, has been identified as one of the fundamental issues to successfully develop solid-state batteries. Understanding the mechanics of lithium at the nanoscale is therefore essential. In this work, the elastic and plastic properties of lithium are measured by nanoindentation within an electron microscope. Lithium metal samples are characterised by electron backscattered diffraction (EBSD) before and after indentation to understand the dependence of the mechanical properties on crystallographic orientation, and determine the stiffness tensor components, moduli and Poisson’s ratio using a method first proposed by Vlassak and Nix. The measured stiffness tensor components are C11=13.3, C12=11.2, and C44=8.8 GPa. Hardness measurements show a clear size effect with hardness in excess of 100 MPa observed for indent depths below 300 nm, which could contribute toward observed lithium filament propagation.

Keywords

lithium metal anode
solid state batteries
mechanical properties

Supplementary materials

Title
Description
Actions
Title
Supporting Information
Description
Supporting Information
Actions

Comments

Comments are not moderated before they are posted, but they can be removed by the site moderators if they are found to be in contravention of our Commenting Policy [opens in a new tab] - please read this policy before you post. Comments should be used for scholarly discussion of the content in question. You can find more information about how to use the commenting feature here [opens in a new tab] .
This site is protected by reCAPTCHA and the Google Privacy Policy [opens in a new tab] and Terms of Service [opens in a new tab] apply.