Under Pressure: Mechanochemical Effects on Structure and Ion Conduction in the Sodium-Ion Solid Electrolyte Na3PS4


Fast-ion conductors are critical to the development of solid-state batteries. The effects of mechanochemical synthesis that lead to increased ionic conductivity in an archetypical sodium-ion conductor Na3PS4 are not fully understood. We present here a comprehensive analysis based on diffraction (Bragg, pair distribution function), spectroscopy (impedance, Raman, NMR, INS) and ab-initio simulations aimed at elucidating the synthesis-property relationships in Na3PS4. We consolidate previously reported interpretations about the local structure of ball-milled samples, underlining the sodium disorder and showing that a local tetragonal framework more accurately describes the structure than the originally proposed cubic one. Through variable-pressure impedance spectroscopy measurements, we report for the first time the activation volume for Na+ migration in Na3PS4, which is ~30% higher for the ball-milled samples. Moreover, we show that the effect of ball-milling on increasing the ionic conductivity of Na3PS4 to ~10-4 S/cm can be reproduced by applying external pressure on a sample from conventional high temperature ceramic synthesis. We conclude that the key effects of mechanochemical synthesis on the properties of solid electrolytes can be analyzed and understood in terms of pressure, strain and activation volume.


Thumbnail image of Na3PS4_mechanical_v10.1.pdf
download asset Na3PS4_mechanical_v10.1.pdf 2 MB [opens in a new tab]

Supplementary material

Thumbnail image of SI_Na3PS4_mechanical_v10.1.pdf
download asset SI_Na3PS4_mechanical_v10.1.pdf 2 MB [opens in a new tab]
SI Na3PS4 mechanical v10.1