Controlled Selectivity for Ethanol Steam Reforming Reaction over Doped CeO2 Surfaces: The Role of Gallium

11 May 2020, Version 1
This content is a preprint and has not undergone peer review at the time of posting.


The ethanol steam reforming reaction, together with the adsorption and decomposition of ethanol was studied on CeO2 and gallium-doped ceria (CeGaOx) by a combined experimental and theoretical approach using infrared spectroscopy (IR), mass spectrometry (MS) and density functional theory (DFT) calculations. At 100°C, different types of monodentate ethoxy species were identified as standing-up (SU) on Ce4+ and lying-down (LD) on Ce4+ and Ga3+, with the alkyl chain more perpendicular or parallel to the surface, respectively. It is suggested that the incorporation of Ga into the ceria lattice changes the decomposition pathway of LD species, which converts to acetate instead of ethylene, attributed to the increased lattice oxygen lability in the Ce-O-Ga interface upon doping and the propensity to form Ga-H surface species. Under ethanol steam reforming conditions, Ga doping of ceria-based materials has a drastic effect by improving the H2:CO2 ratio, changing the product distribution and reducing coke formation.


coke precursors
hydrogen production

Supplementary materials



Comments are not moderated before they are posted, but they can be removed by the site moderators if they are found to be in contravention of our Commenting Policy [opens in a new tab] - please read this policy before you post. Comments should be used for scholarly discussion of the content in question. You can find more information about how to use the commenting feature here [opens in a new tab] .
This site is protected by reCAPTCHA and the Google Privacy Policy [opens in a new tab] and Terms of Service [opens in a new tab] apply.