Extended Interfacial Stability Through Simple Acid Rinsing in a Li-Rich Oxide Cathode Material

16 October 2019, Version 1
This content is a preprint and has not undergone peer review at the time of posting.

Abstract

Layered Li-rich Ni, Mn, Co (NMC) oxide cathodes in Li-ion batteries provide high specific capacities (>250 mAh/g) via O-redox at high voltages. However, associated high-voltage interfacial degradation processes require strategies for effective electrode surface passivation. Here, we show that an acidic surface treatment of a Li-rich NMC layered oxide cathode material leads to a substantial suppression of CO2 and O2 evolution, ~90% and ~100% respectively, during the first charge up to 4.8 V vs. Li+/0. CO2 suppression is related to Li2CO3 removal as well as effective surface passivation against electrolyte degradation. This treatment does not result in any loss of discharge capacity and provides superior long-term cycling and rate performance compared to as-received, untreated materials. We also quantify the extent of lattice oxygen participation in charge compensation (“O-redox”) during Li+ removal by a novel ex-situ acid titration. Our results indicate that the peroxo-like species resulting from O-redox originate on the surface at least 300 mV earlier than the activation plateau region around 4.5 V. X-ray photoelectron spectra and Mn-L X-ray absorption spectra of the cathode powders reveal a Li+ deficiency and a partial reduction of Mn ions on the surface of the acid-treated material. More interestingly, although the irreversible oxygen evolution is greatly suppressed through the surface treatment, our O K-edge resonant inelastic X-ray scattering shows the lattice O-redox behavior largely sustained. The acidic treatment, therefore, only optimizes the surface of the Li-rich material and almost eliminates the irreversible gas evolution, leading to improved cycling and rate performance. This work therefore presents a simple yet effective approach to passivate cathode surfaces against interfacial instabilities during high-voltage battery operation.

Keywords

Li-ion batteries
Li-rich NMC Oxides
Interfacial degradation
Anion Redox
O-redox
DEMS
OEMS
Cathode Electrolyte Interface
Surface passivation

Supplementary materials

Title
Description
Actions
Title
McCloskey SuppInfo
Description
Actions

Comments

Comments are not moderated before they are posted, but they can be removed by the site moderators if they are found to be in contravention of our Commenting Policy [opens in a new tab] - please read this policy before you post. Comments should be used for scholarly discussion of the content in question. You can find more information about how to use the commenting feature here [opens in a new tab] .
This site is protected by reCAPTCHA and the Google Privacy Policy [opens in a new tab] and Terms of Service [opens in a new tab] apply.