XPS of Cold Pressed Multilayered and Freestanding Delaminated 2D Thin Films of Mo2TiC2Tz and Mo2Ti2C3Tz (MXenes)

30 May 2019, Version 1
This content is a preprint and has not undergone peer review at the time of posting.


MXenes, transition metal carbides that are synthesized from the top down by etching of their 3D parent layered solids, the MAX phases, are the latest family of the two-dimensional solids discovered. When the A layers – mostly Al – are etched they are replaced by surface terminations, Tz mainly comprised of O-, OH- and F-terminations. One of the few techniques capable of quantifying these surface terminations is X-ray photoelectron spectroscopy, XPS. Herein, we undertook an XPS study of the out-of-plane ordered MXenes, Mo2TiC2Tz and Mo2Ti2C3Tz, in both multilayered, ML, cold pressed and delaminated thin film forms. The harsh conditions needed to etch these MAX phases into MLs, results in their partial oxidation. The hydroxide used to delaminate the MLs results in further oxidation and a reduction in the F-content. In all cases, etching resulted in a decrease in the Ti to Mo ratio implying that the former atoms are selectively etched. In all but the ML Mo2TiC2Tz case, the Mo to C ratio was also reduced. It follows that the loss of Ti also results in the loss of C atoms. With the exception of the ML Mo2Ti2C3Tz case, the number of termination moles per formula unit, z, was > 2, which is energetically unfavorable and thus unlikely. However, if one assumes that not all of the O signal is coming from terminations but rather from O atoms that replace C atoms in the MX blocks, then z ≈ 2. This work is an important step in quantifying and understanding the effects of etching on terminations and structure in these Mo and Ti-based MXenes.


Mo-based MXenes
X-ray photoelectron spectroscopy
surface chemistry
2D materials

Supplementary materials



Comments are not moderated before they are posted, but they can be removed by the site moderators if they are found to be in contravention of our Commenting Policy [opens in a new tab] - please read this policy before you post. Comments should be used for scholarly discussion of the content in question. You can find more information about how to use the commenting feature here [opens in a new tab] .
This site is protected by reCAPTCHA and the Google Privacy Policy [opens in a new tab] and Terms of Service [opens in a new tab] apply.