Understanding the mechanism of enhanced cycling stability in Sn-Sb composite Na-ion battery anodes: in-operando alloying and diffusion barriers

29 April 2019, Version 1
This content is a preprint and has not undergone peer review at the time of posting.


Sn-Sb composites are of great interest for high capacity sodium ion batteries due to their high stability, but because multiple phases and alloyed compositions are formed during cycling, the roles of each are challenging to deduce. In this work, two approaches were taken to investigate the importance of β-SnSb formation on the cycling stability of Sn-rich Sn-Sb composite sodium-ion battery (SIB) anodes. First, to tease out the role of each component, thin layers of amorphous silicon with thicknesses ranging from 0.5 to 10 nm, were incorporated between Sn and Sb layers, of equal thicknesses. Silicon has low solubility in both tin and antimony, and thus acts as a barrier layer that can interfere with the formation of Sn-Sb alloys. The equivalent composition of this sandwich structure was Sn53Sb47. Upon electrochemical cycling, a clear correlation between capacity retention and Si thickness was observed, and it was found that a 1 nm thick Si layer was sufficient to inhibit the formation of the β-SnSb intermetallic, resulting in loss of the capacity of the tin layer after a few tens of cycles. The second approach involved capping a Sn film with increasingly thicker Sb layers. Thicker antimony layers were found to have a large positive influence on cycling stability with a marked drop-off in the capacity retention when there is not enough Sb to fully convert the bilayer into β-SnSb. These results point to the necessity of the Sn and Sb being in intimate contact prior to cycling for the β-SnSb phase to form in-operando, which is necessary for the excellent capacity retention of the Sn-Sb system.


Sodium ion batteries

Supplementary materials

Sn-Si-Sb trilayer mechanism April25 JMB PDF


Comments are not moderated before they are posted, but they can be removed by the site moderators if they are found to be in contravention of our Commenting Policy [opens in a new tab] - please read this policy before you post. Comments should be used for scholarly discussion of the content in question. You can find more information about how to use the commenting feature here [opens in a new tab] .
This site is protected by reCAPTCHA and the Google Privacy Policy [opens in a new tab] and Terms of Service [opens in a new tab] apply.