Progressive Polytypism and Bandgap Tuning in Azetidinium Lead Halide Perovskites

preprint
submitted on 28.04.2021, 20:26 and posted on 29.04.2021, 13:10 by Jiyu Tian, David Cordes, Alexandra Slawin, Eli Zysman-Colman, Finlay Morrison

Mixed halide azetidinium lead perovskites AzPbBr3-xXx (X = Cl or I) were obtained by mechanosynthesis. With varying halide composition from Cl- to Br- to I-; the chloride and bromide analogs both form in the hexagonal 6H polytype while the iodide adopts the 9R polytype. An intermediate 4H polytype is observed for mixed Br/I compositions. Overall the structure progresses from 6H to 4H to 9R perovskite polytype with varying halide composition. Rietveld refinement of the powder X-ray diffraction patterns revealed a linear variation in unit cell volume as a function of the average radius of the anion, which is not only observed within the solid solution of each polytype (according to Vegard’s law) but extends uniformly across all three polytypes. This is correlated with a progressive (linear) tuning of the bandgap from 3.41 to 2.00 eV. Regardless of halide, the family of azetidinium halide perovskite polytypes are highly stable, with no discernible change in properties over more than 6 months under ambient conditions

History

Email Address of Submitting Author

finlay.morrison@st-andrews.ac.uk

Institution

University of St Andrews

Country

UK

ORCID For Submitting Author

0000-0002-2813-3142

Declaration of Conflict of Interest

no conflict of interest

Exports

ChemRxiv

Exports