Preprints are manuscripts made publicly available before they have been submitted for formal peer review and publication. They might contain new research findings or data. Preprints can be a draft or final version of an author's research but must not have been accepted for publication at the time of submission.
submitted on 16.10.2020 and posted on 16.10.2020by Parveen Kumar Deralia, Aline Maire du Poset, Anja Lund, Anette Larsson, Anna Ström, Gunnar Westman
Herein we present arabinoxylan (AX)-based thermoplastics obtained by ring opening oxidation and subsequent reduction (dA-AX) combined with hydrophobization with three different glycidyl ethers [n-butyl (BuGE), isopropyl (iPrGE) and 2-ethylhexyl (EtHGE) glycidyl ether]. We also present the relationship of structural composition, thermal processing and thermomechanical properties. The BuGE and iPrGE etherified dA-AXs showed glass transition temperatures (Tg) far below their degradation temperatures and gave thermoplastic materials when compression-molded at 140˚C. The BuGE (3 mole) etherified dA-AX films at 19 and 31 % oxidation levels exclusively exhibit 244 % (±42) and 267 % (±72) elongation. In contrast, iPrGE-dA-AX samples with shorter and branched terminals in the side chains had maximum 60 % (±19) elongation. The dramatic difference in elongation is assumed to be due to the presence of longer alkoxide chains, higher molar substitution and dual Tg for the BuGE samples. Such superior elongation of AX thermoplastic films and its relationship with molar substitution and Tg has not been reported before.