An Analysis of the Effect of the Zirconium Precursor of MOF-808 on Its Thermal, Structural, and Surface Properties

revised on 28.08.2018, 16:14 and posted on 28.08.2018, 16:15 by Carolina Ardila-Suárez, Jhonatan Rodriguez-Pereira, Víctor Gabriel Baldovino Medrano, Gustavo E Ramírez-Caballero

Due to their thermal and chemical stability zirconium based Metal-Organic Frameworks (Zr-MOFs) have been extensively studied in the literature. However, many details of the influence of preparation conditions are still unclear. Most papers tend to use one type of metallic precursors for synthesizing Zr-MOFs such as MOF-808. Therefore, as far as we know, a systematic analysis of the effect of the zirconium precursor on the properties of MOF-808 has not been conducted. In this work, three different metallic precursors were employed; namely, zirconium chloride, zirconyl chloride, and zirconyl nitrate for synthesizing MOF-808 keeping all other synthesis conditions constant. The results of the study indicated the following: (i) the nature of the zirconium precursor impacts the crystalline and porous structure of MOF-808. Particularly, the presence of structural water in the precursors causes a detriment in these properties which was reflected in an increase of the relative percentage of amorphicity of the materials as well as on the formation of disorganized mesopores. (ii) In contrast to (i), the surface properties of the materials and their thermal stability under an air atmosphere were not altered by the use of the different precursors. All materials exhibited a surface populated by free and uncoordinated carboxylates as well as inorganic zirconium structures corresponding to uncoordinated oxo-clusters. The ensemble of these findings contributess to a better understanding of the features that make MOFs interesting for diverse applications. Particularly, works on defect engineering may be benefited from the insight on surface chemistry provided in this contribution.


Fundación para la Promoción de la Investigación y la Tecnología, FPIT


Email Address of Submitting Author


Universidad Industrial de Santander



ORCID For Submitting Author


Declaration of Conflict of Interest



Logo branding