Aerosol-Assisted Sol-Gel Synthesis of Mesoporous TiO2 Materials, and Their Use as Support for Ru-Based Methanation Catalysts

11 March 2019, Version 1
This content is a preprint and has not undergone peer review at the time of posting.

Abstract

Mesoporous TiO2 materials have been prepared by an aerosol process, which leverages on the acetic acid-mediated sol-gel chemistry and on the evaporation-induced self-assembly phenomenon to obtain materials with high specific surface area and large mesoporous volume. The obtained spherical particles are calcined to release the porosity. It is shown that the mesoscopic order can be preserved when the calcination is carried out at relatively low temperature (375 °C and below). Harsher calcination conditions lead to the progressive destruction of the mesostructured, concomitant with a progressive drop of textural properties and with the crystallization of larger anatase domains. The mesoporous TiO2 material calcined at 350°C (specific surface area = 260 m².g-1; pore volume = 0.36 cm³.-1; mean pore diameter = 5.4 nm) was selected as a promising support for preformed RuO2 nanoparticles, and subsequently annealed in air. It is shown that the presence of RuO2 nanoparticles and subsequent annealing provoke further intense modification of the texture and crystallinity of the TiO2 materials. In addition to a drop in the textural parameters, a RuO2-mediated crystallization of rutile TiO2 is highlighted at temperature as low as 250°C. After an in situ reduction in H2, the catalysts containing TiO2 rutile and relatively small RuO2 crystals showed the highest activity in the methanation of CO2.

Keywords

CO2
CO2 methanation
TiO2
Mesoporous TiO2
hydrogenation
mesoporous catalysts
Ruthenium

Supplementary materials

Title
Description
Actions
Title
Kim Debecker mesoporous Ru-TiO2 aerosol - preprint - ESI
Description
Actions

Comments

Comments are not moderated before they are posted, but they can be removed by the site moderators if they are found to be in contravention of our Commenting Policy [opens in a new tab] - please read this policy before you post. Comments should be used for scholarly discussion of the content in question. You can find more information about how to use the commenting feature here [opens in a new tab] .
This site is protected by reCAPTCHA and the Google Privacy Policy [opens in a new tab] and Terms of Service [opens in a new tab] apply.